Factory Direct High Quality PUR(Polyurethane) Reactive Hot Melt Adhesive WANLI® PUR-2580 with Viscosity About 4000mPa·s@140℃(Brookfield-ASTMD3236) for Mutual Adhesion of PET, PVC And Other Plastics
Wanli® PUR hot melt adhesive PUR-2580 for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-2580 can be used for mutual adhesion of PET, PVC and other plastics. PUR-2580 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final strength. After curing, PUR-2580 has good peel strength.
APPLICATION
Wanli® PUR hot melt adhesive PUR-2580 is used for flat lamination bonding. PUR-2580 can be used for mutual adhesion of PET, PVC and other plastics.
| Application Material | Woodworking Flat Lamination Hot Melt Adhesives |
| Appearance | Light Yellow & Solid |
| Component | PUR (Polyurethane) |
| Application Industry | Woodworking Flat Lamination Bonding |
| Solid Content | 100 Percent |
| Operating Temperature | 110℃~135℃ |
| Melt Viscosity | Around 4000mPa·s@140℃(Brookfield-ASTMD3236) |
| Open Time | About 5min@25℃ |
| Usage Scope | Flat Lamination Bonding of PET, PVC And Other Plastics |
| Shelf Life | 6 Months |
| Package | 310ml/Aluminum Tube, 2Kg/Bag, 20Kg/Barrel, 200Kg/Barrel |
FEATURE
PUR-2580 is featured stable viscosity under heating at a certain temperature.
High initial bonding strength and final strength.
PUR-2580 has good peel strength after curing.
USER GUIDE
The package of PUR-2580 is suitable for various dispensing equipment.
The recommended operating temperature is 110℃~135℃.
In order to achieve complete curing, it is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity).
STORAGE
Store the product where it’s dry, cool and avoid direct sunlight. The storage temperature should be no more than 35℃ and avoid open fire or heat source.