Wholesale Bulk Quality Textile Lamination Hot Melt Adhesive PUR-6573
Wanli® PUR hot melt adhesive PUR-6573 for textile lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-6573 can be used for bonding various of textiles, such as sponges, leather, fabrics, etc. PUR-6573 is featured stable viscosity under heating at a certain temperature, high initial bonding strength and final bonding strength. After curing, PUR-6573 has good peeling strength, good elasticity, good heat&humidity resistance and chemical resistance.
APPLICATION
Wanli® PUR hot melt adhesive PUR-6573 is used for textile lamination bonding. PUR-6573 can be used for bonding various of textiles, such as sponges, leather, fabrics, etc.
| Application Material | Fabric to Leather Lamination Bonding |
| Appearance | Yellowish Solid |
| Component | PUR (Polyurethane) |
| Application Industry | Textile Lamination |
| Solid Content | 100% |
| Operating Temperature | 110～140 ℃ |
| Melt Viscosity | 4000~6000cps@130℃/6000~8000cps@120℃(Brookfield-ASTM D3236) |
| Open Time | 4-5min @ 25℃ |
| Usage Scope | Fabric to Leather Bonding |
| Shelf Life | 6 Months |
| Package | 310ml/Aluminum Tube, 20Kg/Barrel, 200Kg/Barrel |
FEATURE
Stable viscosity under heating at a certain temperature.
High initial bonding strength and final bonding strength.
Good elasticity.
After curing, it has good peeling strength, good elasticity, good heat&humidity resistance and chemical resistance.
USER GUIDE
The package of PUR-6573 is suitable for various dispensing equipment.
The recommended operating temperature is 110℃~140℃.
In order to achieve complete curing, it is best to place the finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, relative humidity about 65%).
STORAGE
Store PUR-6573 in a dry, cool place, out of direct sunlight. Storage temperature should not exceed 35°C. Avoid open flames or heat sources.