Manufactory Direct Flat Lamination of Decorative Panels Reactive PUR Hot Melt Adhesive WANLI® PUR-9007 with Open Time About 4 Minutes @25℃ And High Initial Bonding Strength & Final Strength, Excellent Heat & Moisture & Chemical Resistance
Wanli® PUR hot melt adhesive PUR-9007 for flat lamination bonding is a single-component reactive PUR hot melt adhesive with 100% solid content. PUR-9007 can be used for bonding metal plates, plastics, paper products, wood-plastic boards, medium density boards, etc. PUR-9007 is featured stable viscosity under heating at a certain temperature, very high initial bonding strength. After curing, PUR-9007 has high peel strength, good heat and humidity resistance and chemical resistance.
APPLICATION
Wanli® PUR hot melt adhesive PUR-9007 is used for flat lamination bonding. PUR-9007 can be used for bonding metal plates, plastics, paper products, wood-plastic boards, medium density boards, etc.
| Application Material | Woodworking Flat Lamination Hot Melt Adhesives |
| Appearance | Yellow & Solid |
| Component | PUR (Polyurethane) |
| Application Industry | Woodworking Flat Lamination Bonding |
| Solid Content | 100% |
| Operating Temperature | 150~160 ℃( Depend On Machine, Substrate, Environment And Other Conditions) |
| Melt Viscosity | About 5000cps@160℃(Brookfield-ASTMD3236) |
| Open Time | About 4min@25℃ |
| Usage Scope | Flat Lamination Bonding of Metal, Plastics, Paper, Wood-plastic, MDF, etc. |
| Shelf Life | 6 Months |
| Package | 2Kg/Carton Barrel, 20Kg/Steel Barrel, 200Kg/Steel Barrel |
FEATURE
Stable viscosity under heating at a certain temperature.
Very high initial bonding strength.
PUR-9007 has high peel strength, good heat and humidity resistance and chemical resistance after curing.
USER GUIDE
The package of PUR-9007 is suitable for various dispensing equipment.
The recommended operating temperature is 150℃~160℃.
It is better to place finished product in a working environment with suitable temperature and humidity (recommended temperature: 23~25℃, about 65% relative humidity) to achieve complete curing.
STORAGE
Dry, cool, avoid direct sunlight, no more than 35℃.